Electron Beam Powder Bed Fusion Additive Manufacturing of Ti6Al4V Alloy Lattice Structures: Orientation-Dependent Fatigue Strength and Crack Growth Behaviour Under Compressive Cyclic Loading
Date
Authors
Supervisor
Item type
Journal Article
Degree name
Journal Title
Journal ISSN
Volume Title
Publisher
Elsevier BV
Abstract
Sufficiently high fatigue strength is required for lattices made using electron beam powder bed fusion (EBPBF) for hip implants and understanding the anisotropic fatigue behaviour of EBPBF lattices is necessary for implant design. In this work, the combined effects of loading direction (LD) and cell orientation of EBPBF-Ti6Al4V lattices on the fatigue strength of the structures under cyclic compressive loading have been studied. Simple cubic (SC) ([001]//LD, [011]//LD and [111]//LD) lattices with a relative density of 0.36 were EBPBF made, tested and examined. The fatigue strength of [001]//LD lattices has been determined to be ∼190 MPa at 5 × 106 cycles, ∼8 times higher than that of [011]//LD or [111]//LD lattices. The low fatigue strength of the non-[001]//LD lattices resulted from crack initiation readily occurring in the high tension locations, which are the top and bottom locations of each unit cell. Sideway growth of cracks leading to fracturing along (001) will be shown. This failure mechanism is absent in [001]//LD lattices and thus their fatigue strength is high. Examining the data in the literature has shown that fatigue strength values of all non-SC lattice structures are low, likely due to the same failure mechanism identified for non-[001]//LD SC lattices in this study.Description
Keywords
Cell orientation, Crack growth, Crack initiation, Stress concentration, 4014 Manufacturing Engineering, 40 Engineering, 0903 Biomedical Engineering, 0912 Materials Engineering, 0913 Mechanical Engineering, Biomedical Engineering, 4003 Biomedical engineering, 4016 Materials engineering, 4017 Mechanical engineering
Source
Journal of the Mechanical Behavior of Biomedical Materials, ISSN: 1751-6161 (Print); 1878-0180 (Online), Elsevier BV, 173, 107201-. doi: 10.1016/j.jmbbm.2025.107201
Publisher's version
Rights statement
© 2025 The Authors. Published by Elsevier Ltd. This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/).