Enhancing Mechanical and Tribological Properties of Epoxy Composites with Ultrasonication Exfoliated MoS₂: Impact of Low Filler Loading on Wear Performance and Tribofilm Formation
Date
Supervisor
Item type
Journal Article
Degree name
Journal Title
Journal ISSN
Volume Title
Publisher
MDPI AG
Abstract
This study highlights the impact of low amounts of MoS₂ quantities on composite performance by examining the effects of ultrasonication exfoliated MoS₂ at different loadings (0.1–0.5 wt%) on the mechanical and tribological parameters of epoxy composites. Even at low concentrations, the ultrasonication and exfoliation procedures greatly improve the dispersion of MoS₂ in the epoxy matrix, enabling its efficient incorporation into the tribofilm during sliding. Optimum mechanical properties were demonstrated by the MoS₂/epoxy composite at 0.3 wt%, including a modulus of elasticity of 0.86 GPa, an ultimate tensile strength of 61.88 MPa, and a hardness of 88.0 Shore D, representing improvements of 61.5%, 35.45%, and 16.21%, respectively. Corresponding tribological tests revealed that high sliding velocity (10 N load, 0.2 m/s) resulted in a 44.07% reduction in the coefficient of friction and an 86.29% reduction in wear rate compared to neat epoxy. The enhanced tribological performance is attributed to the efficient removal and incorporation of MoS₂ into the tribofilm, where it acts as a solid lubricant that significantly reduces friction and wear. Even though an ultra-low amount of filler concentration was added to the composite, a unique finding was the high MoS₂ content in the tribofilm at higher sliding speeds, enhancing lubrication and wear protection. This study establishes that even ultralow MoS₂ content, when uniformly dispersed, can profoundly improve the mechanical and tribological properties of epoxy composites, offering a novel approach to enhancing wear resistance.Description
Source
Nanomaterials, ISSN: 2079-4991 (Print); 2079-4991 (Online), MDPI AG, 14(21), 1744-1744. doi: 10.3390/nano14211744
Publisher's version
Rights statement
© 2024 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/).